APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy

Dettagli del prodotto

Termini di trasporto & di pagamento

Quantità di ordine minimo: 50kg

Prezzo: Negoziabile

Imballaggi particolari: Imballaggio di cartone+scatola di legno

Tempi di consegna: 10-30 giorni

Termini di pagamento: T/T

Capacità di alimentazione: 500 tonnellate/mese

Ottenga il migliore prezzo

Contatta ora

Specificità

Descrizione

Specificità

Evidenziare: 
                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                              APM FeCrAl heating strip, high temperature resistance heating strip, Copper Nickel alloy heating wire
                                                  

Materiale:	Lega fecrale	Grado:	APM
Forma:	Striscia	Spessore:	0,08-2,80 mm
Larghezza:	10-200 millimetri	Superficie:	Brillante / ossidato
Condizione:	Morbido	Resistività:	1,53 Ω·mm²/m
Temperatura operativa massima:	1400°C	Processo di produzione:	Metallurgia della polvere
Applicazione:	Riscaldamento di forni industriali	MOQ:	Negoziabile

Materiale:	Lega fecrale
Grado:	APM
Forma:	Striscia
Spessore:	0,08-2,80 mm
Larghezza:	10-200 millimetri
Superficie:	Brillante / ossidato
Condizione:	Morbido
Resistività:	1,53 Ω·mm²/m
Temperatura operativa massima:	1400°C
Processo di produzione:	Metallurgia della polvere
Applicazione:	Riscaldamento di forni industriali
MOQ:	Negoziabile

Descrizione

APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy

Powder Metallurgy APM FeCrAl Heating Alloy Wire up to 1400°C

This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1400 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces,
electronic industrial furnaces and diffusion furnaces.

Main composition

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main mechanical properties
Tensile Strength at Room Temperature: 650-750MPa
Elongation rate: 15-25%
Hardness: HV220-260
1000ºC Tensile Strength at 1000ºC Temperature 22-27MPa
1000ºC 6MPa High Temperature Durability at 1000 Temperature and 6MPa ≥100h
Main physical properties

Density 7.1g/cm3
Resistivity 1.53×10-6 Ω.m
Resistance Temperature Coefficient(Ct)
Melting point:1500ºC
Maximum Continuous Working Temperature 1400ºC

800ºC	1000ºC	1400ºC
1.03	1.04	1.05

Average linear expansion coefficient

20-800ºC	20-1000ºC	20-1400ºC
14	15	16

Fast life

	1400ºC	1370ºC
Average Fast Life (Hours)	178	>500
Sagging rate after rupture	8	11

1400°C APM Heating Strip for Glass Industry Furnaces Factory price

Tags:

Buoni metropolitana/tubo del cavo 400 della lega di nichel di rame di Monel di resistenza della corrosione per la torre di raffreddamento

Ottenga il migliore prezzo

Prego inviici la vostra richiesta e risponderemo appena possibile voi.

Invii

Rame nichel Alloy Wire

Cavo di resistenza elettrica

Cavo nudo della termocoppia

Lega di Fecral

Cavo di termocoppia

Lega di Nicr

Cavo termico dello spruzzo

Elemento riscaldante della fornace

Lega di precisione

Leghe di rame

Leghe di nichel

Cavo smaltato

Lega ad alta temperatura

Connettore di termocoppia

APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy